This alloy is generally used for "commercial quality" cold rolled steel sheet. It is an economical, general purpose steel grade offering moderate strength and toughness. As a standard grade, 1008 steel is used in many common, low-stress applications. Weldability (spot, projection, butt, and fusion) and brazeability are excellent. Applications include extruded, cold headed, cold upset, and cold pressed parts and forms. It has a very good surface finish that is far superior to hot rolled A36.
Product Parameters
Product Name | 1008 Cold Rolled Steel Plate |
Production Process | Hot Rolling, Cold Rolling |
Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
Width | 100mm-3000mm |
Length | 1m-12m, or Customized Size |
Thickness | 0.1mm-400mm |
Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| Element | Content (%) |
|---|---|
| Iron, Fe | 99.31-99.7 % |
| Manganese, Mn | 0.30-0.50 % |
| Carbon, C | 0.10 % |
| Sulfur, S | 0.050 % |
| Phosphorous, P | 0.040 % |
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 340 MPa | 49300 psi |
| Yield strength (depending on temper) | 285 MPa | 41300 psi |
| Elastic modulus | 190-210 Gpa | 27557-30458 ksi |
| Bulk modulus (typical for steel) | 200 GPa | 29000 ksi |
| Shear modulus (typical for steel) | 80.0 GPa | 11600 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 20 % | 20 % |
| Reduction of area | 45 % | 45 % |
| Hardness, Brinell | 95 | 95 |
| Hardness, Knoop (converted from Brinell hardness) | 113 | 113 |
| Hardness, Rockwell B (converted from Brinell hardness) | 55 | 55 |
| Hardness, Vickers (converted from Brinell hardness) | 98 | 98 |
Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing) | 55 | 55 |
Scope of Application
AISI 1008 carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.
FAQ
Q:What about your price?
A:Our price is very competitive because we are a factory. Pls feel free to contact us if you are interested in our products.
Q:What certifications do your products have?
A:We have ISO 9001, SGS, EWC and other certifications.
Q:What kind of payment terms would you accept?
A:We always do T/T.30% T/T as deposit,70% T/T as balance.
Q:What is your MOQ?
A:We will provide Original Mill Usually 25 tonnes, but it can be adjusted according to your needs and the actual situation of the inventory.
Q:What is the delivery time?
A:10-15 days
PACKING AND DELIVERY
PRODUCT TESTING
CLIENT FEEDBACK
Our factory products comply with CE/EN10204/ASTM/classification society certificates/CASO/BIS and other certificates, and all orders are subject to TPI (SGS/TUV/BV, etc.) inspection
CERTIFICATE OF HONOR
COOPERATIVE PARTNER